Equivalent caracteristic Carbon Glass
Tg 130°C  130°C
Density 1.55 g/cm3  2.1 g/cm3
Flex modulus 110 GPa  45 GPa
Structure 100% UD + Smooth carbon fabric look  80% à 0° and 20% à 90°
Material HR Carbon 12K  E Glass
Tolérance  Ø:+/-0.1 mm Ø:+/-0.05 mm  +/-0.3 mm
Finish Smooth carbon fabric look Grip surface
 
 Fiber Carbon Glass
Density 1.60 g/cm3 2.1 g/cm3
Flex modulus 230 GPa  
Tensile strength 3200 MPa  

tubes drapesv2Nice process for specific stacking. Good dimensional tolerances.

Wrapping process use prepreg fabrics (80% 0° fiber and 20% 90° fiber)

Fabrics is cut after thawing in function of the template piece. After that fabrics are rolled around a mandrel. The machinery realize the compaction of fabrics.
We have different diameter 8 mm of 80 mm (tol +/- 0.05 mm internal diameter and tom +/- 0.1 mm external diameter. To finish, we spool thermoplastic yarn with pressure for ensure a god regularity of the tube.